| Cytotoxicity: | 0 Level |
| Density before sintering(g·cm⁻³): | ≥3.0 |
| Brand Name: | APPLEDENTAL |
| Accelerated aging surface monoclinic phase content: | <15% |
| Density after sintering(g·cm⁻³): | 6.07±0.02 |
| Model Number: | ST-C |
| Transparency(1.0±0.02 mm): | 43% |
| Fracture Toughness: | 5.0MPa·m¹ᐟ² |
| Bending strength after sintering (MPa): | 1200 |
| Place of Origin: | China |
| Chemical solubility after sintering(μg·cm⁻²): | <100 |
| Radioactivity(Bq·g⁻¹): | <0.1 |
| Sintering temperature(℃): | 1530 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹): | 10.4±0.5 |
| Certification: | MDR、CE、ISO、FDA |
| Company Info. |
| FOSHAN JINME MEDICAL TECHNOLOGY CO.LTD |
| Verified Supplier |
| View Contact Details |
| Product List |
Model:ST-C Super Translucency
·Pre-colored
·Super Translucency
·High Durability
·Efficient Fabrication
Pre-colored process design, direct color development after high-temperature sintering, eliminating tedious staining procedures and improving processing efficiency;
Balances ultra-high bending strength with excellent transparency, optimizing aesthetic effects while ensuring the durability of the restoration;
Bending strength up to 1200MPa, transparency 43%, rich colors and outstanding anti-aging performance, suitable for single/three teeth/crowns and full zirconia bridges with more than 4 units and copings, implant abutments and full zirconia crowns, etc.


|